What is G10 fiberglass?
G-10 is a high-pressure fiberglass laminate, a type of composite material. It is created by stacking multiple layers of glass cloth, soaked in epoxy resin, and by compressing the resulting material under heat until the epoxy cures. It is manufactured in flat sheets, most often a few millimeters thick.
What is the tensile strength of G10?
40,000 psi
Properties
| Properties | ||
|---|---|---|
| Tensile Strength | 40,000 psi lengthwise | 35,000 psi crosswise |
| Comprehensive Strength | 68,000 psi flatwise | 35,000 psi edgewise |
| Flexural Strength – .125″ | 55,000 psi lengthwise | 45,000 psi crosswise |
| Modulus of Elasticity – Flexural | 2,700 psi lengthwise | 2,200 psi crosswise |
What is the material G10?
G10/FR-4 is a composite material that consists of glass fabric, electrical grade epoxy resin. The material is extremely strong and stiff, has a low coefficient of thermal expansion, and outstanding electrical properties. G10/FR-4 is widely used as an insulator for electrical and electronic applications.
What is the difference between FR4 and G10?
The main difference between NEMA Grades G10 and FR4 is that FR4 is a fire retardant grade of G10. Therefore, FR4 can be safely substituted where G10 is called for, while G10 can never be substituted where FR4 is called for.
How strong is G10 material?
According to Accurate Plastics technical data for G10, the tensile strength of G10 measures in at 40,000+ PSI lengthwise and at 35,000+ PSI crosswise. Compression strength yields 60,000+ PSI flatwise and 35,000+ PSI edgewise.
What is G10 material used for?
G10 plastic is specified for its extremely high strength and high dimensional stability over a wide temperature and humidity conditions. It is used for electrical insulator materials, terminal boards, busebar insulation, electronic test equipment and electric motor rotor insulation.
Does G-10 melt?
Built from durable fiberglass and epoxy resin, and formed under high temperature and pressure, G-10 is unlike other polymers — it will not melt. G-10 is also resistant to temperature and is extremely lightweight.
What is G-10 phenolic?
Phenolic G-10/FR4 is a continuous woven glass fabric laminated with an epoxy resin. This grade is extremely high in mechanical strength, has low water absorption and dissipation factors and has superior electrical characteristics, which are exhibited over a wide range of temperatures and humidities.
How strong is G10 fiberglass?
G10 is also commonly used for underwater applications due to its strength, durability, and highly water-resistant properties. According to Accurate Plastics technical data for G10, the tensile strength of G10 measures in at 40,000+ PSI lengthwise and at 35,000+ PSI crosswise.
Is G10 material good?
What is G10 used for?
At what temperature does G10 melt?
Both G-10 and FR-4 are rated at 285 degree F continuous operating temperature. Because they are thermosets, no melting will occur with these grades, however charring will be observed after extended periods above this temperature rating.
What is G10 material and where it can be used?
A material made by inserting woven glass fiber impregnated with epoxy resin binder through a laminate, G-10 is widely used in electronics and printed circuit boards because it is not electrically conductive. It doesn’t shrink and holds forms very well ensuring dimensional stability.
What is G10 plastic?
G10 is a high-pressure thermoset plastic laminate consisting of multiple layers of woven fiberglass mesh cloth impregnated with an epoxy resin binder. It can be produced with many layers of the same color, or different colors to achieve a specific cosmetic look. Typical G10 is made of only flat layers. Hogue Inc.
What is G-10 handle material?
Use of G10 Material for Knife Handles – Handles, Grips, Scales & More. What is A G-10 Knife Handle? G-10 is the designation for a glass-based epoxy resin laminate. What that means is that you take a glass-based cloth (fiberglass, in other words), soak it in an epoxy resin, and then using heat and pressure compress it into the shape you want.
What are the mechanical properties of fiberglass?
The most widely used composite material is fiberglass in polyester resin, which is commonly referred to as fiberglass. Fiberglass is lightweight, corrosion resistant, economical, easily processed, has good mechanical properties, and has over 50 years of history.